Photoacid-generating copolymer and associated photoresist composition, coated substrate, and method of forming an electronic device

ABSTRACT

A copolymer includes repeat units derived from an acid-labile monomer, an aliphatic lactone-containing monomer, a C 1-12  alkyl (meth)acrylate in which the C 1-12  alkyl group includes a specific base-soluble group, a photoacid-generating monomer that includes an aliphatic anion, and a neutral aromatic monomer having the formula 
                         
wherein R 1 , R 2 , R 3 , X, m, and R 5  are defined herein. The copolymer is used as a component of a photoresist composition. A coated substrate including a layer of the photoresist composition, and a method of forming an electronic device using the coated substrate are described.

FIELD

The present invention relates to photoacid-generating copolymers useful as components of photoresist compositions.

INTRODUCTION

Chemical compounds that decompose to generate acids when exposed to electron beam or extreme ultraviolet radiation, also known as photoacid generators, are the basis for chemically amplified deprotection or crosslinking of polymers in chemically amplified photoresist compositions for microelectronics fabrication. The photoacid generators are incorporated into photoresist compositions as separate compounds, or as repeat units within copolymers. Existing photoresist compositions provide a useful balance of radiation sensitivity, resolution, and line width roughness. However, there is a desire for photoresists exhibiting increased ultimate resolution, reduced mottling (top roughness), and increased depth of focus without substantially compromising radiation sensitivity and/or line width roughness.

SUMMARY

One embodiment is a copolymer comprising repeat units derived from an acid-labile monomer; an aliphatic, lactone-containing monomer; a base-soluble monomer comprising a 1,1,1,3,3,3-hexafluoro-2-hydroxyprop-2-yl substituent or a —NH—S(O)₂—R^(b) substituent wherein R^(b) is C₁₋₄ perfluoroalkyl; a photoacid-generating monomer comprising an aliphatic anion; and a neutral aliphatic monomer having the formula

wherein R¹, R², and R³ are each independently hydrogen, halogen, C₁₋₆ alkyl, or halogenated C₁₋₆ alkyl; m is 0 or 1; X is —O—, —C(O)—, —C(O)—O—, —S—, —S(O)—, —S(O)₂—, —S(O)₂—N(R⁴)—, —N(R⁴)—S(O)₂—, C₁₋₁₂ hydrocarbylene, —O—(C₁₋₁₂ hydrocarbylene)-, —(C₁₋₁₂ hydrocarbylene)-O—, or —C(O)—O—(C₁₋₁₂ hydrocarbylene)-, wherein R⁴ is C₁₋₆ alkyl; and R⁵ is an unsubstituted or substituted C₁₋₂₄ alkyl.

Another embodiment is a photoresist composition comprising the any of the copolymers described herein.

Another embodiment is a coated substrate comprising: (a) a substrate having one or more layers to be patterned on a surface thereof; and (b) a layer of the photoresist composition over the one or more layers to be patterned.

Another embodiment is a method of forming an electronic device, comprising: (a) applying a layer of the photoresist composition on a substrate; (b) pattern-wise exposing the photoresist composition layer to extreme ultraviolet or electron beam activating radiation; and (c) developing the exposed photoresist composition layer to provide a resist relief image.

These and other embodiments are described in detail below.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows 24 nanometer contact hole performance for Comparative Examples 1 and 2 (FIGS. 1(a) and (d), respectively), 22 nanometer line/space performance for the Comparative Example 1 (FIG. 1(b)), and 17 nanometer line/space performance for Comparative Example 2 (FIG. 1(c)).

FIG. 2 is a plot of dissolution rate as a function of exposure dose for the photoresist compositions of Comparative Examples 1 and 2.

FIG. 3 shows top-down scanning electron microscopy (SEM) images for Comparative Example 3 at 26 nanometer critical dimension, and Comparative Examples 6, and 7, and Examples 1 and 3 at 21 nanometer critical dimension after extreme ultraviolet (EUV) patterning.

FIG. 4, on the left side, shows 26 nanometer line/space performance for the inventive photoresist composition of Example 2 and the comparative photoresist composition of Comparative Example 8; on the right side are corresponding plots of critical dimension versus focus as a function of dose symbolized with different line types.

FIG. 5, on the left side, shows 22 nanometer line/space performance for Example 2 and Comparative Example 8; on the right side are corresponding plots of critical dimension versus focus as a function of dose.

DETAILED DESCRIPTION

The present inventors have determined that the copolymers described herein provide photoresist compositions with increased ultimate resolution, reduced mottling (top roughness), and increased depth of focus without substantially compromising radiation sensitivity and/or line width roughness.

One embodiment is a copolymer comprising repeat units derived from an acid-labile monomer; an aliphatic, lactone-containing monomer; a base-soluble monomer comprising a 1,1,1,3,3,3-hexafluoro-2-hydroxyprop-2-yl substituent or a —NH—S(O)₂—R^(b) substituent wherein R^(b) is C₁₋₄ perfluoroalkyl; a photoacid-generating monomer comprising an aliphatic anion; and a neutral aliphatic monomer having the formula

wherein R¹, R², and R³ are each independently hydrogen, halogen, C₁₋₆ alkyl, or halogenated C₁₋₆ alkyl; m is 0 or 1; X is —O—, —C(O)—, —C(O)—O—, —S—, —S(O)—, —S(O)₂—, —S(O)₂—N(R⁴)—, —N(R⁴)—S(O)₂—, C₁₋₁₂ hydrocarbylene, —O—(C₁₋₁₂ hydrocarbylene)-, —(C₁₋₁₂ hydrocarbylene)-O—, or —C(O)—O—(C₁₋₁₂ hydrocarbylene)-, wherein R⁴ is C₁₋₆ alkyl; and R⁵ is an unsubstituted or substituted C₁₋₂₄ alkyl.

Except as otherwise specified, “substituted” shall be understood to mean including at least one substituent such as a halogen (i.e., F, Cl, Br, I), hydroxyl, amino, thiol, carboxyl, carboxylate, ester (including acrylates, methacrylates, and lactones), amide, nitrile, sulfide, disulfide, nitro, C₁₋₁₈ alkyl, C₁₋₁₈ alkenyl (including norbornenyl), C₁₋₁₈ alkoxyl, C₂₋₁₈ alkenoxyl (including vinyl ether), C₆₋₁₈ aryl, C₆₋₁₈ aryloxyl, C₇₋₁₈ alkylaryl, or C₇₋₁₈ alkylaryloxyl. In the context of the neutral aliphatic monomer, “substituted” shall be understood to mean including at least one substituent such as a halogen (i.e., F, Cl, Br, I), carboxyl, ester (including acrylates, methacrylates, and lactones), amide, nitrile, sulfide, disulfide, nitro, C₁₋₁₈ alkyl, C₁₋₁₈ alkenyl (including norbornenyl), C₁₋₁₈ alkoxyl, C₂₋₁₈ alkenoxyl (including vinyl ether), C₆₋₁₈ aryl, C₆₋₁₈ aryloxyl, C₇₋₁₈ alkylaryl, or C₇₋₁₈ alkylaryloxyl. “Fluorinated” shall be understood to mean having one or more fluorine atoms incorporated into the group. For example, where a C₁₋₁₈ fluoroalkyl group is indicated, the fluoroalkyl group can include one or more fluorine atoms, for example, a single fluorine atom, two fluorine atoms (e.g., as a 1,1-difluoroethyl group), three fluorine atoms (e.g., as a 2,2,2-trifluoroethyl group), or fluorine atoms at each free valence of carbon (e.g., as a perfluorinated group such as —CF₃, —C₂F₅, —C₃F₇, or —C₄F₉).

As used herein, the term “alkyl” includes linear alkyl, branched alkyl, cyclic alkyl, and alkyl groups combining two-way and three-way combinations of linear, branched, and cyclic groups. The alkyl groups can be unsubstituted or substituted. Specific examples of alkyl groups include methyl, ethyl, 1-propyl, 2-propyl, cyclopropyl, 1-butyl, 2-butyl, 2-methyl-1-propyl, tertiary-butyl, cyclobutyl, 1-methylcyclopropyl, 2-methylcyclopropyl, 1-pentyl, 2-pentyl, 3-pentyl, 2-methyl-1-butyl, 3-methyl-1-butyl, 2-methyl-2-butyl, 3-methyl-2-butyl, 2,2-dimethyl-1-propyl (neopentyl), cyclopentyl, 1-methylcyclobutyl, 2-methylcyclobutyl, 3-methylcyclobutyl, 1,2-dimethylcyclopropyl, 2,2-dimethylcyclopropyl, 2,3-dimethylcyclopropyl, 1-hexyl, 2-hexyl, 3-hexyl, 2-methyl-1-pentyl, 3-methyl-1-pentyl, 4-methyl-1-pentyl, 2-methyl-2-pentyl, 4-methyl-2-pentyl, 2-methyl-3-pentyl, 3-methyl-2-pentyl, 3-methyl-3-pentyl, 2,2-dimethyl-1-butyl, 3,3-dimethyl-1-butyl, 3,3-dimethyl-2-butyl, 2,3-dimethyl-1-butyl, 2,3-dimethyl-2-butyl, 1,2,2-trimethylcyclopropyl, 2,2,3-trimethylcyclopropyl, (1,2-dimethylcyclopropyl)methyl, (2,2-dimethylcyclopropyl)methyl, 1,2,3-trimethylcyclopropyl, (2,3-dimethylcyclopropyl)methyl, 2,2-dimethylcyclobutyl, 2,3-dimethylcyclobutyl, (1-methylcyclobutyl)methyl, 1,2-dimethylcyclobutyl, 2,3-dimethylcyclobutyl, (2-methylcyclobutyl)methyl, 1,3-dimethylcyclobutyl, 2,4-dimethylcyclobutyl, (3-methylcyclobutyl)methyl, 1-methylcyclopentyl, 2-methylcyclopentyl, cyclopentylmethyl, cyclohexyl, 1-norbornyl, 2-norbornyl, 3-norbornyl, 1-adamantyl, 2-adamantyl, octahydro-1-pentalenyl, octahydro-2-pentalenyl, octahydro-3-pentalenyl, octahydro-1-phenyl-1-pentalenyl, octahydro-2-phenyl-2-pentalenyl, octahydro-1-phenyl-3-pentalenyl, octahydro-2-phenyl-3-pentalenyl, decahydro-1-naphthyl, decahydro-2-naphthyl, decahydro-3-naphthyl, decahydro-1-phenyl-1-naphthyl, decahydro-2-phenyl-2-naphthyl, decahydro-1-phenyl-3-naphthyl, and decahydro-2-phenyl-3-naphthyl.

The copolymer comprises repeat units derived from an acid-labile monomer. In this context, “acid-labile” means that the monomer is reactive with acid derived from photoacid generator. Acid-labile monomers include carboxylic acid esters, acetals, and ketals.

Illustrative acid-labile carboxylic acid esters include the following unsubstituted and substituted tertiary hydrocarbyl (meth)acrylates

and combinations thereof, wherein R^(a) is —H, —F, —CH₃, or —CF₃.

Illustrative acid-labile acetal- and ketal-substituted monomers include

and combinations thereof, wherein R^(a) is —H, —F, —CH₃, or —CF₃.

In some embodiments, the copolymer comprises repeat units derived from the acid-labile monomer in an amount of 5 to 40 weight percent, specifically 10 to 35 weight percent, more specifically 10 to 30 weight percent, based on the total weight of the copolymer.

In addition to repeat units derived from an acid-labile monomer, the copolymer comprises an aliphatic, lactone-containing monomer. Illustrative examples of aliphatic, lactone-containing monomers include

and combinations thereof, wherein R^(a) is —H, —F, —CH₃, or —CF₃.

In some embodiments, the copolymer comprises repeat units derived from the aliphatic, lactone-containing monomer in an amount of 10 to 70 weight percent, specifically 20 to 60 weight percent, more specifically 25 to 50 weight percent, based on the total weight of the copolymer.

The copolymer further comprises repeat units derived from a base-soluble monomer comprising a 1,1,1,3,3,3-hexafluoro-2-hydroxyprop-2-yl substituent or a —NH—S(O)₂—R^(b) substituent wherein R^(b) is C₁₋₄ perfluoroalkyl. Illustrative examples of such monomers include

and combinations thereof, wherein R^(a) is —H, —F, —CH₃, or —CF₃; and R^(b) is C₁₋₄ perfluoroalkyl.

In some embodiments, the copolymer comprises the repeat units derived from the base-soluble monomer in an amount of 3 to 40 weight percent, specifically 5 to 35 weight percent, more specifically 10 to 30 weight percent, based on the total weight of the copolymer.

The copolymer further comprises repeat units derived from a photoacid-generating monomer comprising an aliphatic anion. In some embodiments, the photoacid-generating monomer is of the formula

wherein R^(a) is —H, —F, —CH₃, or —CF₃; A is ester-containing or non-ester-containing, fluorinated or non-fluorinated C₁₋₂₀ alkylene, or C₃₋₂₀ cycloalkylene; Z⁻ is an anionic moiety comprising sulfonate, sulfonamidate (anion of sulfonamide), or sulfonimidate (anion of sulfonamide); and G⁺ is a sulfonium or iodonium cation.

Illustrative examples of such monomers include

and combinations thereof, wherein R^(a) is —H, —F, —CH₃, or —CF₃.

In some embodiments, the copolymer comprises the repeat units derived from the photoacid-generating monomer in an amount of 2 to 30 weight percent, specifically 2 to 28 weight percent, more specifically 3 to 25 weight percent, based on the total weight of the copolymer.

The copolymer further comprises repeat units derived from a neutral aliphatic monomer having the formula

wherein R¹, R², and R³ are each independently hydrogen, halogen, C₁₋₆ alkyl, or halogenated C₁₋₆ alkyl; m is 0 or 1; X is —O—, —C(O)—, —C(O)—O—, —S—, —S(O)—, —S(O)₂—, —S(O)₂—N(R⁴)—, —N(R⁴)—S(O)₂—, C₁₋₁₂ hydrocarbylene, —O—(C₁₋₁₂ hydrocarbylene)-, —(C₁₋₁₂ hydrocarbylene)-O—, or —C(O)—O—(C₁₋₁₂ hydrocarbylene)-, wherein R⁴ is C₁₋₆ alkyl; and R⁵ is an unsubstituted or substituted C₁₋₂₄ alkyl. In some embodiments, the neutral aliphatic monomer has a calculated Log P (c Log P) value of 2.5 to 6. Within this range the c Log P value can be 2.5 to 5. P is the partition ratio of the monomer between 1-octanol and water. c Log P values can be calculated with, for example, MOLINSPIRATION CHEMINFORMATICS (http://www.molinspiration.com). The “neutral aliphatic monomer” can be referred to as the “aliphatic monomer” for brevity. The structure of the aliphatic monomer has been defined such that it is free of groups that become protonated or react in an acidic medium, and free of groups that become ionized or react in a basic medium. Thus, the copolymer repeat unit derived from the aliphatic monomer will be substantially electrically neutral and chemically unreactive in the presence of photogenerated acid, and in an alkaline developer such as 2.38 weight percent tetramethylammonium hydroxide.

In some embodiments of the aliphatic monomer, R¹ and R² are hydrogen; R³ is —H, —F, —CH₃, or —CF₃; X is —O—, —C(O)—O—, —(C₁₋₁₂ hydrocarbylene)-, —O—(C₁₋₁₂ hydrocarbylene)-, —(C₁₋₁₂ hydrocarbylene)-O—, or —C(O)—O—(C₁₋₁₂ hydrocarbylene)-; and R⁵ is an unsubstituted or substituted C₆₋₁₂ alkyl. In some embodiments, R⁵ is unsubstituted or substituted norbornyl, or unsubstituted or substituted adamantyl.

Illustrative examples of neutral aliphatic monomers include

or a combination thereof, wherein R^(a) is —H, —F, —CH₃, or —CF₃; each occurrence of R^(c) is independently halogen, C₁₋₁₂ hydrocarbyl, C₂₋₁₀ alkenyl, C₁₋₆ perfluoroalkyl, or C₃₋₆ perfluorocycloalkyl; R^(c) is C₁₋₁₀ alkylene or C₃₋₁₀ cycloalkylene; R^(f) is C₁₋₁₂ alkyl, C₁₋₆ perfluoroalkyl, C₃₋₁₀ cycloalkyl, or C₃₋₆ perfluorocycloalkyl; i is 1, 2, 3, or 4; n is 0 or 1; and each occurrence of q is independently 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10.

In some embodiments, the copolymer comprises the repeat units derived from the neutral aliphatic monomer in an amount of 1 to 30 weight percent, specifically 2 to 25 weight percent, more specifically 2 to 20 weight percent, based on the total weight of the copolymer.

In some embodiments, the monomers used to form the copolymer comprise no more than 45 mole percent of monomers comprising an aromatic group. Within this limit, the content of monomers comprising an aromatic group can be 5 to 45 mole percent, specifically 5 to 40 mole percent, more specifically 5 to 35 mole percent.

In some embodiments, the monomers used to prepare the copolymer exclude monomers comprising fluorenyl ester groups. Such monomers are described in U.S. Pat. No. 8,450,042 B2 to Hatakeyama et al.

In some embodiments, the monomers used to prepare the copolymer exclude monomers having both an acid-labile group that generates a base-soluble group (e.g., tertiary-alkyl (meth)acrylate ester), and a base-labile group that generates a group having increased solubility in alkali developer (e.g., a lactone-substituted alkyl (meth)acrylate). Such monomers are described in U.S. Patent Application Publication No. US 2012/0076997 A1 of Hirano et al. Due to the bulky side chain, polymerization of the monomers is expected to be challenging.

In some embodiments, the copolymer has a weight average molecular weight of 1,000 to 50,000 atomic mass units, specifically 2,000 to 30,000 atomic mass units, more specifically 3,000 to 20,000 atomic mass units, still more specifically 3,000 to 10,000 atomic mass units. In some embodiments, the dispersity of the copolymer, which is the ratio of weight average molecular weight to number average molecular weight is 1.1 to 3, specifically 1.1 to 2. Molecular weight values are determined by gel permeation chromatography using polystyrene standards.

In a very specific embodiment, the acid-labile monomer comprises

the aliphatic, lactone-containing (meth)acrylate ester comprises

the base-soluble monomer comprises

the photoacid-generating monomer comprises

the neutral aliphatic monomer comprises

or a combination thereof, wherein R^(a) is —H, —F, —CH₃, or —CF₃; each occurrence of R^(c) is independently halogen, C₁₋₁₂ hydrocarbyl, C₂₋₁₀ alkenyl, C₁₋₆ perfluoroalkyl, or C₃₋₆ perfluorocycloalkyl; R^(c) is C₁₋₁₀ alkylene or C₃₋₁₀ cycloalkylene; R^(f) is C₁₋₁₂ alkyl, C₁₋₆ perfluoroalkyl, C₃₋₁₀ cycloalkyl, or C₃₋₆ perfluorocycloalkyl; i is 1, 2, 3, or 4; n is 0 or 1; and each occurrence of q is independently 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10.

One embodiment is a photoresist composition comprising the copolymer in any of its above-described variations. The photoresist composition can contain the copolymer is an amount of 50 to 99.9 weight percent, based on the total weight of solids (excluding solvent) in the photoresist composition. Within this range, the copolymer content of the photoresist can be 55 to 99.9 weight percent, specifically 65 to 99.9 weight percent.

The photoresist composition can further include one or more photoactive components such as photoacid generators, photobase generators, photoinitiators, additional (meth)acrylate-based polymers with or without bound photoacid generators, hydroxystyrene-based polymers with or without bound photoacid generators, and combinations thereof. The photoresist composition can further comprise polymers other than (meth)acrylate-based polymers and hydroxystyrene-based polymers such as, for example, the aromatic polyacetals described in U.S. Nonprovisional patent application Ser. No. 13/943,169, filed 16 Jul. 2013.

Photoacid generators can produce an acid when exposed to activating radiation, such as EUV radiation (e.g., at 193 nanometers), e-beam radiation, and other radiation sources. Photoacid generators generally include those photoacid generators suitable for the purpose of preparing photoresists. Photoacid generators include, for example, non-ionic oximes and various onium ion salts. Onium ions include, for example, unsubstituted and substituted ammonium ions, unsubstituted and substituted phosphonium ions, unsubstituted and substituted arsonium ions, unsubstituted and substituted stibonium ions, unsubstituted and substituted bismuthonium ions, unsubstituted and substituted oxonium ions, unsubstituted and substituted sulfonium ions, unsubstituted and substituted selenonium ions, unsubstituted and substituted telluronium ions, unsubstituted and substituted fluoronium ions, unsubstituted and substituted chloronium ions, unsubstituted and substituted bromonium ions, unsubstituted and substituted iodonium ions, unsubstituted and substituted aminodiazonium ions (substituted hydrogen azide), unsubstituted and substituted hydrocyanonium ions (substituted hydrogen cyanide), unsubstituted and substituted diazenium ions (RN═N⁺R₂), unsubstituted and substituted iminium ions (R₂C═N⁺R₂), quaternary ammonium ions having two double-bonded substituents (R═N⁺═R), nitronium ion (NO₂ ⁺), bis(trarylphosphine)iminium ions ((Ar₃P)₂N⁺), unsubstituted or substituted tertiary ammonium having one triple-bonded substituent (R≡NH⁺), unsubstituted and substituted nitrilium ions (RC≡NR⁺), unsubstituted and substituted diazonium ions (N≡N⁺R), tertiary ammonium ions having two partially double-bonded substituents (R

N⁺H

R), unsubstituted and substituted pyridinium ions, quaternary ammonium ions having one triple-bonded substituent and one single-bonded substituent (R≡N⁺R), tertiary oxonium ions having one triple-bonded substituent (R≡O⁺), nitrosonium ion (N≡O⁺), tertiary oxonium ions having two partially double-bonded substituents (R

O⁺

R), pyrylium ion (C₅H₅O⁺), tertiary sulfonium ions having one triple-bonded substituent (R≡S⁺), tertiary sulfonium ions having two partially double-bonded substituents (R

S⁺

R), and thionitrosonium ion (N≡S⁺). In some embodiments, the onium ion is selected from unsubstituted and substituted mono- or diaryliodonium ions, and unsubstituted and substituted mono-, di-, and triarylsulfonium ions. Examples of suitable onium salts can be found in U.S. Pat. No. 4,442,197 to Crivello et al., U.S. Pat. No. 4,603,101 to Crivello, and U.S. Pat. No. 4,624,912 to Zweifel et al.

Suitable photo acid generators are known in the art of chemically amplified photoresists and include, for example: onium salts, for example, triphenylsulfonium trifluoromethanesulfonate, (p-tert-butoxyphenyl)diphenylsulfonium trifluoromethanesulfonate, tris(p-tert-butoxyphenyl)sulfonium trifluoromethanesulfonate, triphenylsulfonium p-toluenesulfonate; nitrobenzyl derivatives, for example, 2-nitrobenzyl-p-toluenesulfonate, 2,6-dinitrobenzyl-p-toluenesulfonate, and 2,4-dinitrobenzyl-p-toluenesulfonate; sulfonic acid esters, for example, 1,2,3-tris(methanesulfonyloxy)benzene, 1,2,3-tris(trifluoromethanesulfonyloxy)benzene, and 1,2,3-tris(p-toluenesulfonyloxy)benzene; diazomethane derivatives, for example, bis(benzenesulfonyl)diazomethane, bis(p-toluenesulfonyl)diazomethane; glyoxime derivatives, for example, bis-O-(p-toluenesulfonyl)-α-dimethylglyoxime, and bis-O-(n-butanesulfonyl)-α-dimethylglyoxime; sulfonic acid ester derivatives of an N-hydroxyimide compound, for example, N-hydroxysuccinimide methanesulfonic acid ester, N-hydroxysuccinimide trifluoromethanesulfonic acid ester; and halogen-containing triazine compounds, for example, 2-(4-methoxyphenyl)-4,6-bis(trichloromethyl)-1,3,5-triazine, and 2-(4-methoxynaphthyl)-4,6-bis(trichloromethyl)-1,3,5-triazine. Suitable photoacid generators with specific examples are further described in U.S. Pat. No. 8,431,325 to Hashimoto et al. in column 37, lines 11-47 and columns 41-91.

Two specific PAGS are the following PAG 1 and PAG2, the preparation of which is described in U.S. Patent Application Ser. No. 61/701,588, filed Sep. 15, 2012.

Other suitable sulfonate PAGS include sulfonated esters and sulfonyloxy ketones. See J. of Photopolymer Science and Technology, 4(3):337-340 (1991), for disclosure of suitable sulfonate PAGS, including benzoin tosylate, t-butylphenyl α-(p-toluenesulfonyloxy)-acetate and t-butyl α-(p-toluenesulfonyloxy)-acetate. Preferred sulfonate PAGs are also disclosed in U.S. Pat. No. 5,344,742 to Sinta et al.

Other useful photoacid generators include the family of nitrobenzyl esters, and the s-triazine derivatives. Suitable s-triazine photoacid generators are disclosed, for example, in U.S. Pat. No. 4,189,323.

Photoacid generators further include photo-destroyable bases. Photo-destroyable bases include photo-decomposable cations, and preferably those useful for preparing PAGs, paired with an anion of a weak (pK_(a)>2) acid such as, for example, a C₁₋₂₀ carboxylic acid. Exemplary such carboxylic acids include formic acid, acetic acid, propionic acid, tartaric acid, succinic acid, cyclohexylcarboxylic acid, benzoic acid, salicylic acid, and other such carboxylic acids. Exemplary photo-destroyable bases include those combining cations and anions of the following structures where the cation is triphenylsulfonium or one of the following:

where R is independently H, a C₁₋₂₀ alkyl, a C₆₋₂₀ aryl, or a C₆₋₂₀ alkyl aryl, and the anion is

where R is independently H, a C₁₋₂₀ alkyl, a C₁₋₂₀ alkoxyl, a C₆₋₂₀ aryl, or a C₆₋₂₀ alkyl aryl.

The photoresist can include a photobase generator, including those based on non-ionic photo-decomposing chromophores such as, for example, 2-nitrobenzyl groups and benzoin groups. An exemplary photobase generator is ortho-nitrobenzyl carbamate.

The photoresist can include a photoinitiator. Photoinitiators are used in the photoresist composition for initiating polymerization of the cross-linking agents by generation of free-radicals. Suitable free radical photoinitiators include, for example, azo compounds, sulfur containing compounds, metallic salts and complexes, oximes, amines, polynuclear compounds, organic carbonyl compounds and mixtures thereof as described in U.S. Pat. No. 4,343,885, column 13, line 26 to column 17, line 18; and 9,10-anthraquinone; 1-chloroanthraquinone; 2-chloroanthraquinone; 2-methylanthraquinone; 2-ethylanthraquinone; 2-tert-butylanthraquinone; octamethylanthraquinone; 1,4-naphthoquinone; 9,10-phenanthrenequinone; 1,2-benzanthraquinone; 2,3-benzanthraquinone; 2-methyl-1,4-naphthoquinone; 2,3-dichloronaphthoquinone; 1,4-dimethylanthraquinone; 2,3-dimethylanthraquinone; 2-phenylanthraquinone; 2,3-diphenylanthraquinone; 3-chloro-2-methylanthraquinone; retenequinone; 7,8,9,10-tetrahydronaphthalenequinone; and 1,2,3,4-tetrahydrobenz(a)anthracene-7,12-dione. Other photoinitiators are described in U.S. Pat. No. 2,760,863 and include vicinal ketaldonyl alcohols, such as benzoin, pivaloin, acyloin ethers, e.g., benzoin methyl and ethyl ethers; and alpha-hydrocarbon-substituted aromatic acyloins, including alpha-methylbenzoin, alpha-allylbenzoin, and alpha-phenylbenzoin. Photoreducible dyes and reducing agents disclosed in U.S. Pat. Nos. 2,850,445; 2,875,047; and 3,097,096 as well as dyes of the phenazine, oxazine, and quinone classes; benzophenone, 2,4,5-triphenylimidazolyl dimers with hydrogen donors, and mixtures thereof as described in U.S. Pat. Nos. 3,427,161; 3,479,185; and 3,549,367 can be also used as photoinitiators.

The photoresist composition can further include a surfactant. Illustrative surfactants include fluorinated and non-fluorinated surfactants, and are preferably non-ionic. Exemplary fluorinated non-ionic surfactants include perfluoro C₄ surfactants such as FC-4430 and FC-4432 surfactants, available from 3M Corporation; and fluorodiols such as POLYFOX™ PF-636, PF-6320, PF-656, and PF-6520 fluorosurfactants from Omnova.

The photoresist composition can further include quenchers that are non-photo-destroyable bases. These include, for example, those based on hydroxides, carboxylates, amines, imines and amides. Such quenchers include C₁₋₃₀ organic amines, imines or amides, C₁₋₃₀ quaternary ammonium salts of strong bases (e.g., a hydroxide or alkoxide) or a weak base (e.g., a carboxylate). Exemplary quenchers include amines such as tripropylamine, dodecylamine, tris(2-hydroxypropyl)amine, tetrakis(2-hydroxypropyl)ethylenediamine; aryl amines such as diphenylamine, triphenylamine, aminophenol, and 2-(4-aminophenyl)-2-(4-hydroxyphenyl)propane, Troger's base; hindered amines such as diazabicycloundecene (DBU), diazabicyclononene (DBN), and tetrahydroxy isopropyl diamine and tert-butyl-4-hydroxy-1-piperidiene carboxylate; ionic quenchers including quaternary alkyl ammonium salts such as tetrabutylammonium hydroxide (TBAH), tetramethylammonium 2-hydroxybenzoic acid (TMA OHBA), and tetrabutylammonium lactate. Suitable quenchers are further described in U.S. Pat. No. 8,431,325 to Hashimoto et al.

The photoresist components are typically dissolved in a solvent for dispensing and coating. Exemplary solvents include anisole; alcohols including 1-methoxy-2-propanol, and 1-ethoxy-2 propanol; esters including n-butyl acetate, ethyl lactate, 1-methoxy-2-propyl acetate, methoxyethoxy propionate, ethoxyethoxy propionate, and methyl 2-hydroxyisobutyrate; ketones including cyclohexanone and 2-heptanone; and combinations thereof. The solvent amount can be, for example, 70 to 99 weight percent, specifically 85 to 98 weight percent, based on the total weight of the photoresist composition.

Photoresist compositions also may contain other materials. For example, other optional additives include actinic and contrast dyes, anti-striation agents, plasticizers, speed enhancers and sensitizers. Such optional additives typically will be present in minor concentration in a photoresist composition.

In some embodiments, the photoresist composition in solution comprises the polymer in an amount of 50 to 99.9 weight percent, specifically 55 to 99.9 weight percent, more specifically 65 to 99.9 weight percent, based on the total weight of solids. It will be understood that “polymer” used in this context of a component in a photoresist may mean only the copolymer disclosed herein, or a combination of the copolymer with another polymer useful in a photoresist. The photo-destroyable base may be present in the photoresist in an amount of 0.01 to 5 weight percent, specifically 0.1 to 4 weight percent, more specifically 0.2 to 3 weight percent, based on the total weight of solids. A surfactant may be included in an amount of 0.01 to 5 weight percent, specifically 0.1 to 4 weight percent, more specifically 0.2 to 3 weight percent, based on the total weight of solids. A photoacid generator is included in the amounts of 0 to 50 weight percent, specifically 1.5 to 45 weight percent, more specifically 2 to 40 weight percent, based on the total weight of solids. A quencher may be included in relatively small amounts of for example, from 0.03 to 5 weight percent based on the total weight of solids. Other additives may be included in amounts of less than or equal to 50 weight percent, specifically less than or equal to 35 weight percent, or more specifically less than or equal to 25 weight percent, based on the total weight of solids. The total solids content for the photoresist composition may be 0.5 to 50 weight percent, specifically 1 to 45 weight percent, more specifically 2 to 40 weight percent, and still more specifically 5 to 30 weight percent. It will be understood that total solids includes polymer, photo-destroyable base, quencher, surfactant, any added PAG, and any optional additives, exclusive of solvent.

Another embodiment is a negative tone photoresist comprising the copolymer. Preferred negative-acting compositions comprise a mixture of materials that will cure, crosslink, or harden upon exposure to acid, and one, two, or more photoacid generators as disclosed herein. Preferred negative acting compositions comprise a polymer binder such as a phenolic or non-aromatic polymer, a crosslinker component and a photoactive component of the invention. Such compositions and the use thereof have been disclosed in European Patent Application No. EP0164248 A2 of Feely, and U.S. Pat. No. 5,128,232 to Thackeray et al. Preferred phenolic polymers for use as the polymer binder component include novolaks and poly(vinylphenol)s. Preferred crosslinkers include amine-based materials, including melamine, glycolurils, benzoguanamine-based materials, and urea-based materials. Melamine-formaldehyde polymers are often particularly suitable. Such crosslinkers are commercially available, e.g. the melamine polymers, glycoluril polymers, urea-based polymer and benzoguanamine polymers, such as those sold by Cytec under tradenames CYMEL™ 301, 303, 1170, 1171, 1172, 1123 and 1125 and BEETLE™ 60, 65 and 80.

Another embodiment is a coated substrate comprising: (a) a substrate having one or more layers to be patterned on a surface thereof; and (b) a layer of the photoresist composition over the one or more layers to be patterned.

The substrate can be of a material such as a semiconductor, such as silicon or a compound semiconductor (e.g., III-V or II-VI), glass, quartz, ceramic, copper and the like. Typically, the substrate is a semiconductor wafer, such as single crystal silicon or compound semiconductor wafer, having one or more layers and patterned features formed on a surface thereof. Optionally, the underlying base substrate material itself may be patterned, for example, when it is desired to form trenches in the base substrate material. Layers formed over the base substrate material may include, for example, one or more conductive layers such as layers of aluminum, copper, molybdenum, tantalum, titanium, tungsten, and alloys, nitrides or silicides of such metals, doped amorphous silicon or doped polysilicon, one or more dielectric layers such as layers of silicon oxide, silicon nitride, silicon oxynitride or metal oxides, semiconductor layers, such as single-crystal silicon, underlayers, antireflective layers such as a bottom antireflective layers, and combinations thereof. The layers can be formed by various techniques, for example, chemical vapor deposition (CVD) such as plasma-enhanced CVD, low-pressure CVD or epitaxial growth, physical vapor deposition (PVD) such as sputtering or evaporation, electroplating or spin-coating.

The invention further includes a method of forming an electronic device, comprising: (a) applying a layer of any of the photoresist compositions described herein on a substrate; (b) pattern-wise exposing the photoresist composition layer to activating (e.g., ultraviolet or electron beam) radiation; (c) developing the exposed photoresist composition layer to provide a resist relief image. The method can, optionally, further include (d) etching the resist relief pattern into the underlying substrate.

Applying the photoresist composition to the substrate can be accomplished by any suitable method, including spin coating, spray coating, dip coating, and doctor blading. In some embodiments, applying the layer of photoresist composition is accomplished by spin coating the photoresist in solvent using a coating track, in which the photoresist composition is dispensed on a spinning wafer. During dispensing, the wafer can be spun at a speed of up to 4,000 rotations per minute (rpm), specifically 500 to 3,000 rpm, and more specifically 1,000 to 2,500 rpm. The coated wafer is spun to remove solvent, and baked on a hot plate to remove residual solvent and free volume from the film to make it uniformly dense.

Pattern-wise exposure is then carried out using an exposure tool such as a stepper, in which the film is irradiated through a pattern mask and thereby is exposed pattern-wise. In some embodiments, the method uses advanced exposure tools generating activating radiation at wavelengths capable of high resolution including extreme-ultraviolet (EUV) or electron-beam (e-beam) radiation. It will be appreciated that exposure using the activating radiation decomposes the PAG in the exposed areas and generates acid and decomposition by-products, and that the acid then effects a chemical change in the polymer (deblocking the acid sensitive groups to generate a base-soluble group, or alternatively, catalyzing a cross-linking reaction in the exposed areas) during the post exposure bake (PEB) step. The resolution of such exposure tools can be less than 30 nanometers.

Developing the exposed photoresist layer is then accomplished by treating the exposed layer with a suitable developer capable of selectively removing the exposed portions of the film (where the photoresist is positive tone) or removing the unexposed portions of the film (where the photoresist is crosslinkable in the exposed regions, i.e., negative tone). In some embodiments, the photoresist is positive tone based on a polymer having acid-sensitive (deprotectable) groups, and the developer is preferably a metal-ion-free tetraalkylammonium hydroxide solution, such as, for example, aqueous 0.26 Normal tetramethylammonium hydroxide. Alternatively, negative tone development (NTD) can be conducted by use of a suitable organic solvent developer. NTD results in the removal of unexposed regions of the photoresist layer, leaving behind exposed regions due to polarity reversal of those regions. Suitable NTD developers include, for example, ketones, esters, ethers, hydrocarbons, and mixtures thereof. Other suitable solvents include those used in the photoresist composition. In some embodiments, the developer is 2-heptanone or a butyl acetate such as n-butyl acetate. Whether the development is positive tone or negative tone, a pattern forms by developing.

The photoresist can, when used in one or more such a pattern-forming processes, be used to fabricate electronic and optoelectronic devices such as memory devices, processor chips (including central processing units or CPUs), graphics chips, and other such devices.

The invention is further illustrated by the following examples.

EXAMPLES

The acronyms and chemical structures of monomers used in these examples are presented in Table 1.

TABLE 1 Monomer Acronym Monomer Structure α-GBLMA

CF3PPMA

DiHFA

ECP PDBT- F2

PDBT-F2

PPMA

TBPPDBT- F2

ADMA

Synthesis of a (Comparative) PPMA/α-GBLMA/DiHFA/TBPPDBT-F2 Copolymer.

A feed solution was made by dissolving PPMA (41.2 grams), α-GBLMA (45.35 grams), DiHFA (28.48 grams) and TBP PDBTS-F₂ (13.96 grams) in 130.8 grams of a 30:70 (v/v) mixture of ethyl lactate and gamma-butyrolactone. A heel solution was prepared by dissolving PPMA (2.69 grams), α-GBLMA (2.24 grams), DiHFA (3.92 grams) and TBPPDBTS-F₂ (2.13 grams) in 86.5 grams of a 30:70 (v/v) mixture of ethyl lactate and gamma-butyrolactone. An initiator solution was prepared by dissolving 14.6 grams of the azo initiator 2,2′-azobis(2,4-dimethyl valeronitrile) (obtained as V-65 from Wako Pure Chemical Industries, Ltd.) in 14.6 grams of a 2:1 (v/v) mixture of acetonitrile and tetrahydrofuran (THF).

The polymerization was carried out in a 2-liter, 3-neck round bottom flask fitted with a water condenser and a thermometer to monitor the reaction in the flask. The contents were stirred using an overhead stirrer. The reactor was charged with the heel solution and the contents were heated to 75° C. The feed solution and the initiator solution were fed into the reactor using syringe pumps over a 4 hour time period. The contents were then stirred for additional 2 hours, after which the reaction was quenched using hydroquinone (2.0 grams). The contents were cooled to room temperature, diluted with THF to 25 weight percent, and precipitated twice out of 10-fold (by weight) of a 95:5 (w/w) mixture of diisopropyl ether (IPE) and methanol (MeOH). After each precipitation step, the polymer obtained was dried under vacuum at 50° C. for 24 hours to yield 99 grams of a PPMA/α-GBLMA/DiHFA/TBPPDBT-F2 copolymer having the respective repeat units in a 34:50:10:6 mole ratio and a weight average molecular weight of 5,300 atomic mass units. This copolymer is designated Copolymer 1.

Synthesis of a (Comparative) CF3PPMA/α-GBLMA/DiHFA/PDBT-F2 Copolymer.

A similar procedure was used to prepare a CF3PPMA/α-GBLMA/DiHFA/PDBT-F2 copolymer having the respective repeat units in a 36:47:11:6 mole ratio and a weight average molecular weight of 5,000 atomic mass units. This copolymer is designated Copolymer 2.

Lithographic Evaluation of PPMA/α-GBLMA/DiHFA/TBPPDBT-F2 and CF3PPMA/α-GBLMA/DiHFA/PPDBT-F2 Copolymers.

Table 2 summarizes the compositions and processing conditions for photoresists incorporating the PPMA/α-GBLMA/DiHFA/TBPPDBT-F2 and CF3PPMA/α-GBLMA/DiHFA/PDBT-F2 copolymers. In table two, component amounts are expressed in weight percent based on total solids excluding solvents. In Table 2, the photoacid generator DiMADMeOAC PDBT-ADOH has the chemical structure

Also in Table 2, “PDQ” is photodecomposable quencher. The PDQ TBPPDBT-ADCA has the chemical structure

The quencher THIPDA has the chemical structure

The surfactant POLYFOX™ PF-656, obtained from OMNOVA SOLUTIONS INC., has the chemical structure

where x+y is, on average, about 6. “EL” is ethyl lactate, “HBM” is methyl 2-hydroxybutyrate.

TABLE 2 Comparative Example 1 Comparative Example 2 Copolymer 75.02% Copolymer 1 99.75% Copolymer 2 PAG 23.67% DiMADMeOAC none PDBT-ADOH PDQ, 1.0016% TBPPDBT- 0.149% THIPDA Quencher ADCA, 0.225% THIPDA Surfactant 0.075% POLYFOX ™ 0.0998% POLYFOX ™ solution PF-656 in 70:30 PF-656 in 70:30 (w/w) EL/HBM (w/w) EL/HBM Soft bake 110° C. for 90 seconds 130° C. for 90 seconds conditions Post-exposure 100° C. for 60 seconds 100° C. for 60 seconds bake conditions

FIG. 1 shows contact hole and line/space performance for the Comparative Example 1 photoresist, which was optimized for contact hole exposures, and the Comparative Example 2 photoresist, which was optimized for line exposures. For Comparative Example 1, 30 nanometer contact holes were well printed at 51 millijoules/centimeter² with a critical dimension uniformity (CDU) of 2.82 nanometers (FIG. 1(a)). However, when the same resist was evaluated for line/space application, resolution was limited by pattern collapse at 22 nanometers half pitch (FIG. 1(b)). For Comparative Example 2, a 17 nanometer resolution line/space was obtained (FIG. 1(c)), but the contact hole performance (FIG. 1(d)) was significantly worse than that of Comparative Example 1.

To address the question of why a contact hold resist fails in a line/space exposure and a line/space resist fails in a contact hole exposure, the above photoresist compositions were analyzed by monitoring the dissolution rate (DR) in tetramethylammonium hydroxide developer (0.26 Normal tetramethylammonium hydroxide, a standard developer used in the positive tone development) under 248 nanometer exposure. The dissolution rate data plotted in FIG. 2 were generated using a dissolution rate monitoring tool, LTJ ARM 800, employing a 470 nanometer monitoring wavelength. In the FIG. 2 plot, the x-axis is exposure dose, expressed in units of millijoules/centimeter² and plotted on a log scale, and the y-axis is dissolution rate, expressed in units of nanometers/second and plotted on a log scale. The Comparative Example 1 photoresist exhibits a higher R_(max) value (about 7586 nanometers/second) and a steep contrast (Tan θ). In contrast, the Comparative Example 2 photoresist was characterized by a much shallower dissolution contrast and lower R_(max) and R_(min). The difference in performance of these resists is consistent with the difference in dissolution rates.

Since dissolution rate would be dependent on acid labile group content in the copolymer, three PPMA/α-GBLMA/DiHFA/PDBT-F2 copolymers with different levels of acid-labile monomers were synthesized and are summarized in Table 3. The 36/45/11/5 copolymer is the control system with 36 mole percent acid-labile monomer. The other two copolymers were synthesized with 26 and 21 mole percent acid-labile monomer. Each copolymer had a weight average molecular weight of about 5,000 atomic mass units.

TABLE 3 Copolymer Monomers Monomer Ratio 3 PPMA/α-GBLMA/DiHFA/PDBT-F2 36:48:11:5 4 PPMA/α-GBLMA/DiHFA/PDBT-F2 26:57:11:6 5 PPMA/α-GBLMA/DiHFA/PDBT-F2 21:63:8:8

Photoresist compositions containing Copolymers 3-5 were formulated as summarized in Table 4, where component amounts are based on total solids, excluding solvents.

TABLE 4 Photoresist C. Ex. 3 C. Ex. 4 C. Ex. 5 Copolymer 99.75% Copolym. 99.75% Copolym. 99.75% Copolym. 3 4 5 Quencher 0.15% THIPDA 0.15% THIPDA 0.15% THIPDA Surfactant 0.0998% 0.0998% 0.0998% solution POLYFOX ™ POLYFOX ™ POLYFOX ™ PF-656 in 70:30 PF-656 in 70:30 PF-656 in 70:30 (w/w) EL/HBM (w/w) EL/HBM (w/w) EL/HBM Soft-bake 110° C. for 90 110° C. for 90 110° C. for 90 conditions seconds seconds seconds Post-exposure 100° C. for 60 100° C. for 60 100° C. for 60 bake seconds seconds seconds conditions

Photolithographic results are presented in Table 5, where “UFTL” is the unexposed film thickness loss, expressed in Angstroms, “R_(min),” is the dissolution rate of unexposed resist expressed in nanometers per second, “R_(max)” is the dissolution rate of fully exposed resist expressed in nanometers per second, and “248 nm E₀” is the 248 nanometer exposure dose to clear expressed in millijoules/centimeter². The results show that the copolymers with lower acid-labile monomer contents exhibited significant reductions in R_(max). Since the UFTL values for Comparative Examples 4 and 5 were significantly elevated, they were not evaluated by EUV lithography. A high UFTL could potentially impart severe top loss (mottling) and reduce the aspect ratio after the development cycle.

TABLE 5 UFTL R_(min) R_(max) 248 nm E₀ Photoresist (Å) (nm/s) (nm/s) (mJ/cm²) C. Ex. 3 8 0.005 6930 27 C. Ex. 4 29 0.03 3376 24 C. Ex. 5 54 0.04 1935 24

Additional copolymers were synthesized to explore the effects of incorporating the neutral aliphatic monomer, ADMA. The copolymer compositions are summarized in Table 6. Copolymer 8 was synthesized as follows. A heel solution was made by dissolving PPMA (0.44 grams), α-GBLMA (0.36 grams), DiHFA (0.63 grams) and TBPPDBT-F2 (0.34 grams) in 16.35 grams of a 70:30 (v/v) mixture of gamma-butyrolactone and ethyl lactate. A feed solution was prepared by dissolving PPMA (4.78 grams), α-GBLMA (7.25 grams), DiHFA (4.78 grams), ADMA (2.07 grams) and TBPPDBT-F2 (2.57 grams) in 21.16 grams of a 70:30 (v/v) mixture of gamma-butyrolactone and ethyl lactate. An initiator solution was prepared by dissolving 2.34 gram of the azo initiator 2,2′-azobis(2,4-dimethyl valeronitrile) (obtained from Wako Pure Chemical Industries, Ltd.) in 2.34 grams of 2:1 (v/v) mixture of acetonitrile and tetrahydrofuran. The polymerization was carried out in a 300 milliliter, three-neck round-bottom flask fitted with a water condenser and a thermometer to monitor the reaction temperature in the flask. The reactor was charged with the heel solution and the contents were heated to 75° C. The feed solution and initiator solution were fed into the reactor using syringe pumps over a period of 4 hours. The contents were then stirred for an additional 2 hours, after which the reaction was quenched using hydroquinone (0.2 grams). The contents were cooled to room temperature, diluted with THF to 25 weight percent, and precipitated twice out of 10-fold (by weight) of a 95:5 (w/w) mixture of diisopropyl ether and methanol. The polymer obtained after each precipitation step was dried under vacuum at 50° C. for 24 hours to yield 8 grams of PPMA/α-GBLMA/DiHFA/ADMA/TBPPDBT-F2 copolymer (Copolymer 6). Other polymers listed in Table 6 were synthesized in a similar way except for a change in the type and/or content of the neutral monomer employed.

TABLE 6 Copolymer Monomers Monomer Ratio 6 PPMA/α-GBLMA/DiHFA/TBPPDBT-F2 35/48/12/5 7 PPMA/α-GBLMA/DiHFA/TBPPDBT-F2 26/58/11/5 8 PPMA/α-GBLMA/DiHFA/TBPPDBT-F2/ 26/47/12/5/10 ADMA 9 PPMA/α-GBLMA/DiHFA/TBPPDBT-F2/ 16/47/12/5/20 ADMA 10 PPMA/α-GBLMA/DiHFA/ECPPDBT-F2 36/47/12/5

Photoresist compositions containing Copolymers 6-10 were formulated as summarized in Table 7, where component amounts are based on total solids, excluding solvents. The photoacid generator TBPPDBT DHC has the chemical structure

All formulations in Table 7 used a 70:30 (w/w) mixture of ethyl lactate and gamma-butyrolactone as solvent. The resists were processed at a soft bake of 110° C. for 90 seconds and a post-exposure base at 100° C. for 60 seconds. Contrast curves at 248 nanometers were generated by coating the resist on a 60 nanometer thick organic antireflective layer (Dow Electronic Materials AR™ 9-900). The resist was exposed at 248 nanometers on a Canon TELACT tool. After post-exposure bake, the resists were developed for 60 seconds using 0.26 Normal tetramethylammonium hydroxide solution. Film thickness values were measured using KLA Tencore OPTIPROBE™ 7341 thermal wave tool.

TABLE 7 Photoresist Copolymer Quencher PAG surfactant C. Ex. 6 99.75% 0.149% none 0.099% Copolymer 6 THIPDA POLYFOX ™ PF-656 C. Ex. 7 99.75% 0.149% none 0.099% Copolymer 7 THIPDA POLYFOX ™ PF-656 Ex. 1 99.75% 0.149% none 0.099% Copolymer 8 THIPDA POLYFOX ™ PF-656 Ex. 2 72.56% 0.82% 26.5% 0.072% Copolymer 8 THIPDA TBPPDBT POLYFOX ™ DHC PF-656 Ex. 3 99.75% 0.149% none 0.099% Copolymer 9 THIPDA POLYFOX ™ PF-656 Ex. 4 72.56% 0.82% 26.5% 0.072% Copolymer 9 THIPDA TBPPDBT POLYFOX ™ DHC PF-656 C. Ex. 8 72.37% 1.085% 26.4% 0.072% Copolymer 12 TIPA TBPPDBT POLYFOX ™ DHC PF-656 *TIPA = triisopropylamine

Photolithographic results are summarized in Table 8 for the photoresist compositions of Table 7. In Table 8, “EUV Es” is the sizing energy, expressed in millijoules/centimeter², at 26 nanometer critical dimension using extreme ultraviolet exposure. For the photoresist compositions with no added PAG (Comparative Examples 6 and 7, and Examples 1 and 3), the inventive photoresists of Examples 1 and 3 incorporated a copolymer with repeat units derived from a neutral aliphatic monomer, exhibited lower R_(max) values relative to Comparative Example 6, in which the copolymer that does not incorporate a neutral aliphatic monomer, and Comparative Examples 7, in which the copolymer that does not incorporate a neutral aliphatic monomer and does have a lower content of acid-labile groups. It was also observed that the incorporation of the neutral aliphatic monomer in the Copolymers of Examples 1 and 3, even with lower acid labile group content, yields a UFTL which was significantly lower than that of the photoresist in Comparative Example 7. This result is unlike the one shown in Table 5, where the decrease in the acid labile group content in the copolymer was associated with a significant increase in UFTL. For the photoresist compositions of Comparative Example 8 and Examples 2 and 4, which contain added PAG in the formulation, the inventive photoresists of Examples 2 and 4, in which the copolymer incorporates a neutral aliphatic monomer, exhibited much lower R_(max) values relative to Comparative Example 8. A higher UFTL and R_(min) were observed for all formulations containing added PAG as opposed to low UFTL and R_(min) for compositions without added PAG.

TABLE 8 EUV Es 248 nm E₀ 26 nm CD UFTL R_(min) R_(max) Photoresist (mJ/cm²) (mJ/cm²) (Å) (nm/s) (nm/s) Tanθ C. Ex. 6 38 15.29 4 0.005 4500 12 C. Ex. 7 45 15.29 16 0.01 2400 12 Ex. 1 61 24.3 1 0.005 1697 12 Ex. 2 43 21.2 14 0.01 1831 15 Ex. 3 103 — 3 0.004 166 11 Ex. 4 75 45.5 15 0.017 1341 10 C. Ex. 8 36 14.0 13 0.009 7374 18

The Example 3 photoresist was not evaluated for EUV lithography due to slow photo speed. The Example 2 and Comparative Example 8 photoresists were evaluated for line/space performance at the Albany eMET tool. The photoresists were coated at a 40 nanometer thickness on a silicon wafer that had been pre-coated at a 25 nanometer thickness with a polyester-based antireflective layer. The Examples 1 and 4 and Comparative Examples 6 and 7 photoresists were evaluated at the Lawrence Berkeley National Laboratory (LBNL) eMET tool. The photoresists were coated at 35 nanometer thickness (Example 1) or 50 nanometer thickness (Example 4 and Comparative Examples 6 and 7) on an antireflective layer. The resist was pre-baked at 110° C. for 90 seconds followed by a pattern-wise exposure with EUV light. After post-exposure bake at 100° C. for 60 seconds, the resist was developed with 0.26 Normal tetramethylammonium hydroxide for 30 seconds. FIG. 3 shows the 26 nanometer line/space performance for the inventive photoresist of Example 1 and 3, and comparative photoresists of Comparative Examples 3, 6, and 7. The top-down scanning electron micrographs of the inventive photoresists of Examples 1 and 3 exhibit a reduction in mottling at overexposure (21 nanometer critical dimension).

FIG. 4 shows the 26 nanometer line space performance for the inventive photoresist of Example 2 and the comparative photoresist of Comparative Example 8. The inventive photoresists of Example 2 exhibits a reduction in mottling and increase in depth of focus.

FIG. 5 shows the 22 nanometer line/space performance for Example 2 and Comparative Example 8. The inventive photoresists of Example 2 exhibits a reduction in mottling and increase in depth of focus. 

The invention claimed is:
 1. A copolymer comprising repeat units derived from an acid-labile monomer; an aliphatic, lactone-containing monomer; a base-soluble monomer comprising a 1,1,1,3,3,3-hexafluoro-2-hydroxyprop-2-yl substituent or a —NH—S(O)₂—R^(b) substituent wherein R^(b) is C₁₋₄ perfluoroalkyl; a photoacid-generating monomer comprising an aliphatic anion, wherein the photoacid-generating monomer comprises

or a combination thereof, wherein R^(a) is —H, —F, —CH₃, or —CF₃; and a neutral aliphatic monomer comprising

wherein R^(a) is —H, —F, —CH₃, or —CF₃; each occurrence of R^(c) is independently halogen, C₁₋₆ perfluoroalkyl, or C₃₋₆ perfluorocycloalkyl; and q is 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10; or

wherein R^(a) is —H, —F, —CH₃ or —CF₃; each occurrence of R^(c) is independently halogen, C₁₋₁₂ hydrocarbyl, C₂₋₁₀ alkenyl, C₁₋₆ perfluoroalkyl, or C₃₋₆ perfluorocycloalkyl; and each occurrence of q is independently 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10; or

wherein R^(a) is —H, —F, —CH₃, or —CF₃; each occurrence of R^(c) is independently halogen, C₁₋₁₂ hydrocarbyl, C₂₋₁₀ alkenyl, C₁₋₆ perfluoroalkyl, or C₃₋₆ perfluorocycloalkyl; and each occurrence of q is independently 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10; or

wherein R^(a) is —H, —F, —CH₃, or —CF₃; each occurrence of R^(c) is independently halogen, C₁₋₁₂ hydrocarbyl, C₂₋₁₀ alkenyl, C₁₋₆ perfluoroalkyl, or C₃₋₆ perfluorocycloalkyl; R^(c) is C₁₋₁₀ alkylene or C₃₋₁₀ cycloalkylene; n is 1; and each occurrence of q is independently 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10; or

wherein R^(a) is —H, —F, —CH₃, or —CF₃; each occurrence of R^(c) is independently halogen, C₁₋₁₂ hydrocarbyl, C₂₋₁₀ alkenyl, C₁₋₆ perfluoroalkyl, or C₃₋₆ perfluorocycloalkyl; R^(f) is C₁₋₁₂ alkyl, C₁₋₆ perfluoroalkyl, C₃₋₁₀ cycloalkyl, or C₃₋₆ perfluorocycloalkyl; and each occurrence of q is independently 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10; or a combination thereof.
 2. The copolymer of claim 1, wherein the neutral aliphatic monomer has a cLogP of 2.5 to
 6. 3. The copolymer of claim 1, wherein the acid-labile monomer comprises an unsubstituted or substituted tertiary hydrocarbyl (meth)acrylate comprising

or a combination thereof; wherein R^(a) is —H, —F, —CH₃, or —CF₃.
 4. The copolymer of claim 1, wherein the base-soluble monomer comprises

or a combination thereof, wherein R^(a) is —H, —F, —CH₃, or —CF₃; and R^(b) is C₁₋₄ perfluoroalkyl.
 5. The copolymer of claim 1, wherein the acid-labile monomer comprises

wherein the aliphatic, lactone-containing (meth)acrylate ester comprises

wherein the base-soluble monomer comprises

and wherein the photoacid-generating monomer comprises


6. A photoresist composition comprising the copolymer of claim
 1. 7. A coated substrate comprising: (a) a substrate having one or more layers to be patterned on a surface thereof; and (b) a layer of the photoresist composition of claim 6 over the one or more layers to be patterned.
 8. A method of forming an electronic device, comprising: (a) applying a layer of a photoresist composition of claim 6 on a substrate; (b) pattern-wise exposing the photoresist composition layer to activating radiation; and (c) developing the exposed photoresist composition layer to provide a resist relief image.
 9. A copolymer comprising repeat units derived from an acid-labile monomer comprising a carboxylic acid ester having a polycyclic leaving group; an aliphatic, lactone-containing monomer; a base-soluble monomer comprising a 1,1,1,3,3,3-hexafluoro-2-hydroxyprop-2-yl substituent or a —NH—S(O)₂—R^(b) substituent wherein R^(b) is C₁₋₄ perfluoroalkyl; a photoacid-generating monomer comprising an aliphatic anion; wherein the aliphatic anion is

wherein R^(a) is —H, —F, —CH₃, or —CF₃; and a neutral aliphatic monomer comprising

wherein R^(a) is —H, —F, —CH₃, or —CF₃; each occurrence of R^(c) is independently halogen, C₁₋₆ perfluoroalkyl, or C₃₋₆ perfluorocycloalkyl; and q is 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10; or

wherein R^(a) is —H, —F, —CH₃ or —CF₃; each occurrence of R^(c) is independently halogen, C₁₋₁₂ hydrocarbyl, C₂₋₁₀ alkenyl, C₁₋₆ perfluoroalkyl, or C₃₋₆ perfluorocycloalkyl; and each occurrence of q is independently 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10; or

wherein R^(a) is —H, —F, —CH₃, or —CF₃; each occurrence of R^(c) is independently halogen, C₁₋₁₂ hydrocarbyl, C₂₋₁₀ alkenyl, C₁₋₆ perfluoroalkyl, or C₃₋₆ perfluorocycloalkyl; and each occurrence of q is independently 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10; or

wherein R^(a) is —H, —F, —CH₃, or —CF₃; each occurrence of R^(c) is independently halogen, C₁₋₁₂ hydrocarbyl, C₂₋₁₀ alkenyl, C₁₋₆ perfluoroalkyl, or C₃₋₆ perfluorocycloalkyl; R^(c) is C₁₋₁₀ alkylene or C₃₋₁₀ cycloalkylene; n is 1; and each occurrence of q is independently 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10; or

wherein R^(a) is —H, —F, —CH₃, or —CF₃; each occurrence of R^(c) is independently halogen, C₁₋₁₂ hydrocarbyl, C₂₋₁₀ alkenyl, C₁₋₆ perfluoroalkyl, or C₃₋₆ perfluorocycloalkyl; R^(f) is C₁₋₁₂ alkyl, C₁₋₆ perfluoroalkyl, C₃₋₁₀ cycloalkyl, or C₃₋₆ perfluorocycloalkyl; and each occurrence of q is independently 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10; or a combination thereof.
 10. The copolymer of claim 9, wherein the polycyclic leaving group comprises an adamantyl group.
 11. The copolymer of claim 9, wherein the acid-labile monomer is selected from the group consisting of

and combinations thereof, wherein R^(a) is —H, —F, —CH₃, or —CF₃.
 12. The copolymer of claim 9, wherein the photoacid-generating monomer comprises

or a combination thereof, wherein R^(a) is —H, —F, —CH₃, or —CF₃.
 13. A photoresist composition comprising the copolymer of claim
 9. 14. A coated substrate comprising: (a) a substrate having one or more layers to be patterned on a surface thereof; and (b) a layer of the photoresist composition of claim 13 over the one or more layers to be patterned.
 15. A method of forming an electronic device, comprising: (a) applying a layer of a photoresist composition of claim 13 on a substrate; (b) pattern-wise exposing the photoresist composition layer to activating radiation; and (c) developing the exposed photoresist composition layer to provide a resist relief image.
 16. A copolymer comprising repeat units derived from an acid-labile monomer; an aliphatic, lactone-containing monomer; a base-soluble monomer comprising a 1,1,1,3,3,3-hexafluoro-2-hydroxyprop-2-yl substituent or a —NH—S(O)₂—R^(b) substituent wherein R^(b) is C₁₋₄ perfluoroalkyl; a photoacid-generating monomer comprising an aliphatic anion, wherein the aliphatic anion is

wherein R^(a) is —H, —F, —CH₃, or —CF₃; and a neutral aliphatic monomer comprising

wherein R^(a) is —H, —F, —CH₃, or —CF₃; each occurrence of R^(c) is independently halogen, C₁₋₆ perfluoroalkyl, or C₃₋₆ perfluorocycloalkyl; and q is 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10; or

wherein R^(a) is —H, —F, —CH₃ or —CF₃; each occurrence of R^(c) is independently halogen, C₁₋₁₂ hydrocarbyl, C₂₋₁₀ alkenyl, C₁₋₆ perfluoroalkyl, or C₃₋₆ perfluorocycloalkyl; and each occurrence of q is independently 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10; or

wherein R^(a) is —H, —F, —CH₃, or —CF₃; each occurrence of R^(c) is independently halogen, C₁₋₁₂ hydrocarbyl, C₂₋₁₀ alkenyl, C₁₋₆ perfluoroalkyl, or C₃₋₆ perfluorocycloalkyl; and each occurrence of q is independently 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10; or

wherein R^(a) is —H, —F, —CH₃, or —CF₃; each occurrence of R^(c) is independently halogen, C₁₋₁₂ hydrocarbyl, C₂₋₁₀ alkenyl, C₁₋₆ perfluoroalkyl, or C₃₋₆ perfluorocycloalkyl; R^(c) is C_(hio) alkylene or C₃₋₁₀ cycloalkylene; n is 1; and each occurrence of q is independently 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10; or

wherein R^(a) is —H, —F, —CH₃, or —CF₃; each occurrence of R^(c) is independently halogen, C₁₋₁₂ hydrocarbyl, C₂₋₁₀ alkenyl, C₁₋₆ perfluoroalkyl, or C₃₋₆ perfluorocycloalkyl; R^(f) is C₁₋₁₂ alkyl, C₁₋₆ perfluoroalkyl, C₃₋₁₀ cycloalkyl, or C₃₋₆ perfluorocycloalkyl; and each occurrence of q is independently 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10; or a combination thereof. 